High Strength Titanium Plate manufacturing process
Ti belongs to precious metal, its relative density is small, Titanium Plate its strength is high and its strength is high. Below I will introduce the titanium and titanium plate quality corrosion-resistant properties, know titanium pump, titanium plate pump can use the occasion and role. Titanium Plate In a specific environment with excellent corrosion resistance. Titanium pump, titanium plate pump is a strong corrosion-resistant pump, suitable for alkali acid, it is also called alkali acid pump. Its strong corrosion resistance, the key is titanium this metal.
Corrosion resistance of titanium and titanium plates The titanium material has a high degree of stability in a neutral or weakly acidic oxide solution, for example, Titanium Plate titanium and titanium plates in the 100℃fecl100℃ CuC12, 100 ℃ HgC1: (all concentrations), 60% of ALCL2 and 100 ℃ all concentrations of NaCl are stable, Many other oxides of titanium, which are also stable in 100% acetic acid and 100% of acetic acid, Titanium Plate make titanium and titanium plates widely used in these solutions.
Titanium and titanium plates in gasoline, toluene, phenol, formaldehyde, trichloroethylene, acetic acid, citric acid, a chloro-June, etc. have a high corrosion resistance, but in the boiling point and not inflated, titanium in the mass fraction less than 25% of formic acid will be seriously corroded, Titanium Plate in the solution containing acetic anhydride, titanium is not only a serious overall corrosion, and will produce pitting, for many organic synthesis process contact complex organic medium, such as in the production of propylene oxide, phenol, Titanium Plate acetone, chloroacetic acid and other chemical medium, titanium and titanium plate corrosion resistance is better than other structural materials of stainless steel yang.
Titanium and Titanium plate for the ionic oxidant solution also has a high degree of stability, such as 100qC sodium chlorite solution, oxygen water, gas (up to 75 ℃), Titanium Plate hydrogen peroxide containing sodium hydroxide solution and so on. Titanium and titanium plates in wet chlorine corrosion resistance more than other commonly used metals, this is because chlorine has a strong oxidation, Titanium Plate titanium and titanium plate in wet chlorine can be in a stable state of blunt, in order to maintain the titanium in the chlorine in the blunt, need a certain amount of water. Critical water content and oxygen pressure, Titanium Plate velocity, temperature and other factors, but also with titanium equipment or parts of the shape of the size of the surface and mechanical damage of titanium, therefore, the literature on the titanium in oxygen passivation of the critical water content is inconsistent, generally considered that the mass fraction of 0. 01%~0. 5% can be used as the critical water content of titanium in oxygen, but practical experience points out that, in order to ensure the safe use of titanium equipment in oxygen, Titanium Plate sometimes the water quality fraction of 0.6% is not enough, need up to 1. 5%. Titanium Plate The critical water content is also increased with the increase of chlorine temperature and the decrease of airflow velocity.
Titanium plate manufacturing process/titanium plate editing
Hot forging: forging process of metal recrystallization temperature.
Hot rolling: rolling process at higher than recrystallization temperature.
Cold rolling: the plastic deformation temperature is lower than the rolling process of the recovery temperature.
Annealing: a metal heat treatment process that slowly heats the metal to a certain temperature, maintains sufficient time, and then cools at a suitable rate (usually by slow cooling, sometimes controlled cooling).
Pickling: an aqueous solution of sulfuric acid is used to remove films such as oxide on the metal surface.It is the pretreatment or intermediate treatment of electroplating, enamel, rolling, etc.