Search
  • e
  • 527

Email

TEL

CONTACT

Address

Room 703,No.28 Huahai Road.Economic and technical development zone,Shenyang P.R.China

ZIP:110143 

ABOUT       NEWS      PRODUCTS      CAPACITY      NETWORK      MESSAGE      CONTACT

+86-024-25558500

 

WE ARE COMMITTED TO PROVIDING CUSTOMERS WITH

HIGH QUALITY PRODUCTS,COMPETITIVE PRICES AND EXCELLENT SERVICES

 

All rights reserved Shenyang Bona Titanium Technology Co.,Ltd. 辽icp备17016579号Powered by300.cn shenyang.300.cn

Company News
Industry News
Exhibition

Titanium Bars Cleaning

Page view
[Abstract]:
1,TitaniumBarsalkalinewashing:with3-5%ofthenano-nano-solutionofpuresolutionsoak30-60minutes,thetemperatureofabout40degrees.Bestinultrasoniccleaningmachines.Aftersoakingwithdeionizedwaterorwatersprayed
1, Titanium Bars alkaline washing: with 3-5% of the nano-nano-solution of pure solution soak 30-60 minutes, the temperature of about 40 degrees. Best in ultrasonic cleaning machines. After soaking with deionized water or water sprayed inside and outside to neutral, measured conductivity. With pure air ≥ 0.4Mpa pressure drying.
 
2, pickling: 5% nitric acid solution soak for 8 hours or more, the temperature is 40 degrees. Best in ultrasonic cleaning machines. After soaking with deionized water or water sprayed inside and outside to neutral, measured conductivity. With pure air ≥ 0.4Mpa pressure drying.
 
3, the above two methods can be used alone, can also be used in conjunction with each other. If the conditions can be combined with ultrasonic cleaning machine the best results.
 
4, organic pollution can be combined with surfactant cleaning, cell debris pollution system combined with enzyme cleaning effect is more ideal.
 
(Food and beverage can be used to clean the high concentration of citric acid) Note: regular online anti-washing, (online cleaning with pure compressed air or filter solution or clean water recoil) can reduce the number of times with the above method of cleaning.
 
The filter, with high pressure, strong acid, alkali, corrosion resistance, Titanium Bars filter can be used repeatedly and other characteristics, is the use of powder metallurgy method of titanium powder is not through the high temperature sintering method of hollow filter tube, it is widely used In the food, beverage, pharmaceutical, chemical and other industries of liquid-solid separation, especially in the pharmaceutical industry for large infusion and injection production line decarburization filter. This series of products with a compact and beautiful design according to GMP standard production, pipe fittings using international standard quick connection, Titanium Bars easy disassembly and cleaning.
 
Titanium rod filter in the use of a period of time, will produce a certain degree of congestion, performance: flow reduction, filtration front pressure increased, Titanium Bars such as: from 0.22mPa below 0.3mPa higher than the time, then the filter should be cleaned, cleaning method Generally have the following:
 
1. For the newly used filter, the general use of water recoil, gas blowing method to clean, that is slightly larger than the working pressure (such as: 0.3mPa) in the opposite direction of water water cleaning. Recoil time is about 1 to 3 minutes.
 
2. For multiple backwashing, Titanium Bars the filter effect is not obvious recovery time, can be less than 5% hydrochloric acid solution, Titanium Bars or 8% sulfuric acid solution, or 10% NaOH solution at room temperature soak, and then washed with water.
 
Alpha alloy contains a certain amount of stable alpha, which is mainly composed of alpha.It has a small weight, good thermal strength, good weldability and excellent corrosion resistance. The disadvantage is that the room temperature is low, usually used as heat resistant material and corrosion resistant material.Alpha alloys are usually divided into all-alpha alloys (TA7), near-alpha alloys (ti-8al-1m-to-1v) and alpha alloys with a small number of compounds (ti-2.5 Cu).
 
 
 
 
 
 