1, Titanium Bars alkali Wash: Use $number hydroxide to analyze pure solution soak for 30-60 minutes, temperature is about 40 degrees. The best in the ultrasonic cleaning machine. After soaking with filtered deionized water or injecting water inside and outside the neutral, Titanium Bars to measure the conductivity. Blow dry with pure air ≥ 0.4Mpa pressure.

 

 

 

2, Pickling: 5% nitrate solution soaked for more than 8 hours, the temperature is 40 degrees. The best in the ultrasonic cleaning machine.Titanium Bars  After soaking with filtered deionized water or injecting water inside and outside the neutral, to measure the conductivity. Blow dry with pure air ≥ 0.4Mpa pressure.

 

 

 

3, the above two methods can be used alone, can also be used interchangeably with each other. Titanium Bars If conditions, can be combined with ultrasonic cleaning machine effect of the best.

 

 

 

4, organic pollution can be combined with surfactant cleaning, cell debris pollution system combined with enzyme cleaning effect is more ideal.

 

 

 

(Food and beverages can be high concentrations of citric acid cleaning) Note: To often on-line backwashing, (on-line cleaning with pure compressed air or filtered liquid or clean water recoil) can reduce the number of cleaning methods above.

 

 

 

 

 

Titanium Rod Filter uses titanium Powder Sintered filter, which is generally used in coarse filtration or intermediate filtration. This filter has high precision, high temperature resistance, Titanium Bars corrosion resistance, high mechanical strength, widely used in the pharmaceutical industry, shell materials for 316L or 304 stainless steel. comply with GMP standards.

 

1. Avoid scratching, dust and oil.

 

 

 

2. In use, its working pressure should not exceed rated working pressure.

 

 

 

3. Normal use, at least 3-5 minutes of low pressure start-up time, the relative pressure should be controlled under 0.5MPA, and then work pressure gradually to normal needs (maximum pressure of not more than 0.4MPA).

 

 

 

4. After the operation of this product to a certain period, may be due to the blockage of filter elements, resulting in increased pressure flow, need to recoil or backwash regeneration. The regenerative cycle depends on the rated pressure and flow